News
News Highlights
- Books
Featured Books
- smt007 Magazine
Latest Issues
Current IssueIPC APEX EXPO 2024 Pre-show
This month’s issue devotes its pages to a comprehensive preview of the IPC APEX EXPO 2024 event. Whether your role is technical or business, if you're new-to-the-industry or seasoned veteran, you'll find value throughout this program.
Boost Your Sales
Every part of your business can be evaluated as a process, including your sales funnel. Optimizing your selling process requires a coordinated effort between marketing and sales. In this issue, industry experts in marketing and sales offer their best advice on how to boost your sales efforts.
The Cost of Rework
In this issue, we investigate rework's current state of the art. What are the root causes and how are they resolved? What is the financial impact of rework, and is it possible to eliminate it entirely without sacrificing your yields?
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - smt007 Magazine
Under the Hood: Solder Joint Reliability
May 21, 2018 | Burton Carpenter, NXP Semiconductors Inc.Estimated reading time: 3 minutes
The automotive industry continues to drive increased solder joint reliability (SJR) for under-the-hood applications. One aspect of SJR, temperature cycle on board (TCoB) assesses thermal fatigue resistance of solder interconnection between component and PCB during temperature excursions. In some instances, requirements on number of cycles to first failure have increased 2x over previous product generations.
It has been long established that packages using NSMD BGA pads were more resilient than ones with SMD pads to fatigue-induced solder joint cracks. However, NSMD pads in our previous investigations on 292MAPBGA and 416PBGA packages failed sooner in AATS testing due to an alternate failure mode: substrate Cu trace cracks.
Detailed failure analysis revealed that these cracks occurred exclusively on BGA pads in the die shadow. This led to the idea that a mixed design—NSMD pads outside the die shadow, while maintaining SMD pads under the die—could perform better than a pure SMD design.
Separately, lower CTE substrate dielectric materials were under investigation as a means to reduce package warpage. Below Tg, the mold compound CTE is 9ppm/°C. The standard substrate dielectric CTE is 16ppm/°C, resulting in considerable package warpage at lower temperatures. It was hypothesized that lowering the substrate dielectric material CTE to 11ppm/°C would reduce package warpage which in turn should reduce solder joint strain thereby increasing solder joint lifetime.
Table 1: Package details. DOE variables in yellow.
A six-cell experimental matrix was run to study the impact of these two variables (substrate dielectric material and package pad design type.) These experiments used standard daisy-chain temperature cycle testing methodology. Assemblies were monitored in situ to detect failures as they occurred, and 2-parameter Weibull failure distributions were fit to the data. Various metrics derived from the Weibull fits were regressed against the DOE variables to determine which had significant impact on solder joint lifetime, and to what degree.
Crack growth was assessed using cross-section and dye-and-pry techniques on unmonitored assemblies that were removed from the chambers at fixed read points. Conclusions on the impact of the parameters were determined based on the totality of electrical test and crack growth data.
EXPERIMENTAL:
Design
The package attributes are summarized in Table 1. Those highlighted in yellow were varied in the experiment. The substrate dielectric details are in Table 2.
BGA arrays are shown in Figure 1. The baseline SMD design in Figure 1a contained only SMD pads. Hybrid-A in Figure 1b used the same footprint, but the outer four rings were substituted with NSMD pads, while the pads at the die edge were maintained as SMD.
Table 2: Substrate dielectric mechanical properties.
By contrast, the outer six rings were NSMD for Hybrid-B, encompassing the die edge. In all cases, the SMD pad SRO (solder resist opening) was 0.45mm. To compensate for solder wetting down the pad sidewall, the NSMD pads on the hybrid designs were slightly smaller to produce a similar ball height.
These packages were daisy-chain test vehicles with pairs of solder joints electrically connected. A complete circuit was created by connecting pairs on the PCB side that were skipped on the package. All solder joints were monitored as one “net.” A failure on any solder joint meant the remaining solder joints could no longer be electrically monitored.
Figure 1: BGA footprint showing arrangement of SMD and NSMD pads for the three different designs.
Except where parameters were intentionally varied, the daisy-chain packages were mechanically similar to the final products: same die size, area and thickness. Similarly, the same material sets were used: mold compound, die attach, and assembly factory.
To read the full version of this article, which appeared in the April 2018 issue of SMT007 Magazine, click here.
Suggested Items
Indium Corporation, Industry Partners to Showcase Products “Live@APEX”
03/26/2024 | Indium CorporationIndium Corporation®, in cooperation with its industry partners, will feature its proven solder solutions live on the show floor throughout IPC APEX Expo from Apr. 9‒11 in Anaheim, Calif., U.S.
ITW EAE Wins New Product Introduction Award for Electrovert® Wave Soldering Machine Deep Wave
03/26/2024 | ITW EAEITW EAE is proud to announce that it has earned a 2024 New Product Introduction (NPI) Award for Electrovert’s Deep Wave option for wave soldering machines. This new, innovative system provides the ability to pump up to a 20 mm wave height.
Mek's Next-Gen AOI Technology Takes Center Stage at IPC APEX EXPO 2024
03/19/2024 | MEKMek is excited to announce its presence at IPC APEX EXPO, North America's largest electronics manufacturing event, in Anaheim, California, from April 6-11, 2024. Attendees are invited to visit Mek at booth #1433 to explore the latest AOI technology offerings.
Nihon Superior Sets New Standards in Lead-Free Soldering Technology at APEX 2024
03/13/2024 | PVANihon Superior Co. Ltd., an advanced joining material supplier, will exhibit in Booth 1325 during the 2024 IPC APEX EXPO, scheduled to take place April 9-11, 2024 at the Anaheim Convention Center in California.
Apollo Seiko Presents the Next Frontier in Non-Contact Soldering at 2024 IPC APEX EXPO
03/12/2024 | Apollo SeikoApollo Seiko, a leading innovator in soldering technology, is pleased to announce plans to showcase its latest advancements at Booth 1408 during the 2024 IPC APEX EXPO, taking place April 9-11, 2024 at the Anaheim Convention Center in California.