“HASLEN: An Obituary to Black Pad”--a bold title, bound to attract attention and provoke controversy. The term "Black Pad" has been used since the late '90s to describe a type of solder joint failure associated with electroless nickel immersion gold (ENIG) PCB finishes, where solder separates from from the electroless nickel surface leaving a black or dark grey deposit. Many theories have been considered as to the cause, but recent research suggests the effect originates from hypercorrosion of the nickel-phosphorus deposit during the immersion gold plating process.

A webinar presented by ITRI Innovation introduced a new solderable finish known as HASLEN, combining features of two established technologies to deposit solder directly on to electroless nickel by hot air solder leveling, and made possible by novel fluxes based on deep eutectic solvents. The HASLEN finish was claimed to reduce cost and to offer overall improvements in the longevity and reliability of PCB assemblies when compared with ENIG.

A background perspective was provided by Nick Hoo, Materials Technology manager at ITRI Innovation, who summarised the characteristics of currently available solderable finishes for PCBs and focused on the properties of ENIG: Its excellent solderability and solderability retention on storage and after multiple reflow, good planarity, low substrate dissolution, and low intermetallic growth during soldering or in the solid state because of the nickel diffusion barrier between tin and copper in the final joint. Set against these attributes were the disadvantages of high cost and loss of high frequency signal integrity, and issues such as black pad, nickel passivation, gold coating porosity and nickel-copper migration.

Hoo shared the opinion that black pad was a consequence of excessive corrosion of the nickel coating during the immersion gold process, although the term appeared to have become a catch-all for problems encountered with ENIG coatings. He referred to an observation, made during the EU-funded ASPIS project when ionic liquid technology had been investigated as a basis of alternative plating methods, that the properties of certain ionic liquids offered scope for development as soldering fluxes for electronics applications.

The University of Leicester, a collaborator in the ASPIS project, has been for many years the centre for research in ionic liquids, resulting in the development of many specialist metal finishing applications. Dr. Andrew Ballantyne described how a class of ionic liquids known as deep eutectic solvents (DES), which were low cost and environmentally benign, exhibited an exceptional ability to dissolve metal oxides without the use of acids. Used as the basis of soldering fluxes, these materials could effectively clean metal surfaces and prevent metal oxidation during soldering, and had been shown to be effective on a range of metals, some of which had been considered unsolderable using conventional fluxes. 

Share




Suggested Items

Real Time with… IPC APEX EXPO 2023: Jesse Session Talks R&D at Taiyo

01/11/2023 | Nolan Johnson, I-Connect007
Nolan Johnson checks in with Taiyo America’s Technical Manager, Jesse Session, about the new and exciting developments cooking in Taiyo’s R&D department. The company’s groundbreaking inkjet solder mask product line is expanding to meet the needs of customers looking for updated color options that retain the same quality standards and reliability that have come to define Taiyo’s offerings.

Preventing De-wetting Defects In Immersion Tin Soldering

01/04/2023 | Britta Schafsteller, Atotech
Immersion tin is well accepted as a high-reliability final finish in the industry. Due to its excellent corrosion resistance, it exhibits major market shares, particularly in the automotive industry. During the soldering process, an intermetallic compound (IMC) is formed between copper and tin. One remaining concern in the industry is the potential impact of the IMC on the solderability of the final finish. In this article, typical failure modes in soldering immersion tin are described and correlated to potential root causes for the defects.

Taiyo: Reopening Europe for Solder Mask

12/19/2022 | Nolan Johnson, I-Connect007
Nolan Johnson and Stuart Down discuss Taiyo’s partnership with Ventec and how both companies are leveraging their expertise to blaze a trail into the European PCB market. Stuart shares his outlook on the market and the unique challenges posed by global political instability and supply chain constraints, as well as how Europe’s evolving chemical regulations have impacted solder mask formulation. With their sights set on ramping up manufacturing capabilities, Taiyo sees a secure path forward to establishing a sizeable market presence in this promising region.



Copyright © 2023 I-Connect007 | IPC Publishing Group Inc. All rights reserved.